High flame retardant and high electrical performance PVC materials for cable are a PVC-based pellet material which is produced by mixing and granulating with accessory ingredients such as plasticizers, toughening cold, filler ( flame retardant ) , stabilizers , lubricants and colorants.
1. Model, name and application of products
|
Model |
name |
application |
|
HG-70 |
High flame retardant PVC sheath materials at 70 ℃ |
High flame retardant sheath for wire and cable at the thermal class of 70 ℃ |
|
HGZ-90 |
High flame retardant PVC sheath materials at 90 ℃ |
High flame retardant sheath for wire and cable at the thermal class of 90 ℃ |
|
HGD-90 |
High electrical performance PVC sheath materials at 90 ℃ |
Sheath for medium or high-voltage wire and cable at the thermal class of 90 ℃ |
|
HGDZ-90 |
High electrical performance and flame retardant PVC sheath materials at 90 ℃ |
Flame retardant sheath for medium or high-voltage wire and cable at the thermal class of 90 ℃ |
2. Executive Standard
Q/WRD 003-2016
3. Products properties
The products properties are shown in Table 7.
4. Processing
Single screw extruder is used in processing, with the aspect ratio of screw L/D≥20. The recommended reference processing temperature is shown below:
|
Sections |
Section 1 |
Section 2 |
Section 3 |
Section 4 |
Extrusion head |
Die |
|
Temperature/℃ |
150±10 |
160±10 |
165±5 |
170±5 |
170±5 |
170±5 |
5. Packaging, transportation and storage
Package: net weight of each bag (25±0.2) kg. The inner bag is polyethylene film and the outer bag is craft paper composites.
Transportation and storage: no exposure to sunshine and rain during transportation. It should be stored in clean, cool, dry and ventilated warehouse.
Table 7 Products properties
|
Test items |
HGZ-70 |
HGZ-90 |
HGD-90 |
HGDZ-90 |
|
Tensile strength/MPa ≥ |
|
|
|
|
|
Tensile strain at break/% ≥ |
|
|
|
|
|
Thermal deformation ≤ |
|
|
|
|
|
Impact brittle property |
Test temperature /℃ |
|
|
|
|
|
Impact brittle property |
Pass |
Pass |
Pass |
Pass |
|
Thermal stabilization time at 200℃/min ≥ |
|
|
|
|
|
volume resistivity at 20℃/Ω·m ≥ |
|
|
|
|
|
dielectric strength /（MV/m）≥ |
|
|
|
|
|
Oxygen Index/% ≥ |
|
|
|
|
|
Thermal aging test temperature/℃ |
|
|
|
|
|
Thermal aging test time/h |
|
|
|
|
|
Tensile strength after aging/MPa ≥ |
|
|
|
|
|
The biggest change rate of tensile strength/% |
|
|
|
|
|
Tensile strain at break after aging/% ≥ |
|
|
|
|
|
The biggest change rate of tensile strain at break/% |
|
|
|
|
|
Mass loss of thermal aging |
Test temperature/
℃ |
|
|
|
|
|
Test time/h |
|
|
|
|
|
Mass loss/(g/cm2) ≤ |
|
|
|
|